Product Details:
Payment & Shipping Terms:
|
| Applicable Industries: | Industry | Type: | Crusher Hammerhead |
|---|---|---|---|
| Machine Type: | Crusher | Material: | High Manganese Steel, High Manganese Steel, High Chromium For Hammer Head |
| Processing Type: | Casting | Use: | Ore Mining |
| Casting Technology: | Sand Casting,lost Foam Foundry ,v-process Foundry | Applicable Materials: | Granite, Basalt, Limestone, Cement Clinker, Quartz, Iron Ore, Bauxite |
| Heat Treatment: | Anneal, Quenching, Tempering | Testing: | Hardness, Flaw Detector Test |
| Applications: | Gravel Quarry, Concrete Sand, Dry Mortar, Sand | Usage: | Crushing |
| Certificate: | ISO9001:2000/ BV/ China Patent No. 200810049101.2 | Product Name: | Crusher Hammerhead |
| Quality Guarantee: | Crusher Hammerhead Manufacturer | Port: | QingDao,ShangHai,TianJin |
Crusher hammerhead manufacturer
Crusher hammer such as clinker crusher hammer and raw material hammer is one of the core parts of hammer crusher.Our hammer crusher parts:crusher hammer use refining, vacuum casting,directional solid and etc technicals to increase the grain refinement and make the hammers performance achieve the best performance. Hammer hardness is the most essential factor in determining hammer life so the hammer head must be extremely hard and resistant to wear. Our company uses a specical method of heat treating that make the hammer hardness and wear resistance reach the best state of cooperation, thus greatly improve hammer’s service life time. According to the material, our crusher hammer can be dividede into: high manganese hammer, high chrome hammer, bimetal composited hammer. The bimetal composite hammer, our national patent product, is called “Hard Stone Killer” by many clients. Our crusher hammer generally can save users 1/3 equipment investment, saving 1/2 the power consumption, save a lot of maintenance costs.
The alloy steel material that be crushed by hammer crusher is a tremendous difference. The crusher has different forms and hammers. In the condition of crush hard and tough material such as iron raw, Our high Cr bimetal hammer could bear the cutting from the material but easy be come off or break for the hammer’s toughness property is not good. Though the toughness of supper Mn steel is higher but the wear resistant property is not enough. So hammer and blow bar made from high Mn imbedding cemented carbide is the best choice.
The High Mn imbedding cemented carbide hammer(Inlaid Alloy Hammer / alloy hammer/hammer mill) product made by our company use the wear resistant bar made from higher content nano-sized tungsten carbide and titanium carbide. The Rockwell hardness of wear resistant bar is 80HRA~90HRA. We will make the hammer’s matrix with high Mn or super high Mn according to the complexity of hammer mill. We make sure of the 100% metallurgical bonding of the alloy steel material bar surface and matrix by the method of blowing argon at bottom of furnace, diversified qualitative change, diversified inoculation, and appropriate casting, smelting, heat treating.These processing measure increase the combination property of the High Mn imbedding cemented carbide products made by our company. This kind of alloy steel material hammer is widely used in hammer mill. We meet with great favor from our customers at home and abroad.
Details of crusher hammerhead:
|
High Mn Imbedding Cemented Carbide Hammer |
|
|
Alloy steel material |
High Mn with Tungsten Titanium Alloy Rod |
|
Control |
Spectrometer chemical analysis and control while producing |
|
Moulding process |
Water-glass sand casting or lost form mould casting |
|
Melting facility |
Medium frequency electric furnace |
|
Heat treatment |
Anneal, quenching, tempering |
|
Quality Guarantee |
One year against manufacturing defeat |
|
Testing |
Hardness, flaw detector test |
|
Suit Filed |
Cement, mining,quarry,electricity and metallurgy companies |
|
Certificate |
ISO9001:2000/ BV/ China Patent No. 200810049101.2 |
Specifications of crusher hammerhead :
|
Standard |
Chemical component % |
|||||
|
C |
Mn |
Si |
Cr |
S |
P |
|
|
ZG120Mn13Cr2 |
1.05~1.35 |
11~14 |
0.3~0.9 |
1.5~2.5 |
≤0.04 |
≤0.04 |
|
ZG120Mn17Cr2 |
1.05~1.35 |
16~19 |
0.3~0.9 |
1.5~2.5 |
||
|
Notes:Allowed to join trace V,Ti,Ba and RE and so on. |
||||||
The mechanical properties crusher hammerhead:
|
Standard |
Lower yield strength Rel |
Tensile strength Rm |
The section elongation A% |
Shock absorption KU2 |
Hardness HBW |
|
ZG120Mn13Cr2 |
≥390 |
≥735 |
≥20 |
— |
≤300 |