Name: | Grinding Steel Ball | Diameter(mm): | D20-125MM |
---|---|---|---|
Material B2: | Cr: 0.20-0.60 | Material B3: | Cr: 0.70-0.90 |
Hardness: | HRC60-62 | Application: | In Bearing, Hardware, Electronics, Iron Art, Mechanical Equipment |
Composition: | C, Si, Mn, Cr, P, S, Ni, Cu | Classification: | Castings And Forgings |
High Light: | Forging Steel Grinding Media Ball,20mm forged steel grinding media balls,180mm Forging Media Ball |
Forging Steel Grinding Media Ball For Ball Mill (Dimensions: 20mm To 180mm)
1. Technical standard of grinding steel ball:
(1) Hardness test is the most important data for whether the grinding steel ball is wear-resistant, which can be tested by Rockwell hardness tester. Practice shows that the service life of steel balls with HRC60 and above is more than twice of HRC40-50.
(2) Low chromium steel ball refers to chromium content ≤3.0%, carbon content between 1.80%-3.30% of the steel ball is low chromium ball, the national standard requirements of low chromium ball hardness (HRC) must be ≥45 degrees above, if the use of low chromium ball quality recommendations must use heat treatment tempering or vibration aging treatment. If the test hardness (HRC) is below 40 degrees, the low chromium ball hardness is insufficient or overburning.
(3) Application field:
Grinding steel balls are widely used in metallurgical mines, cement building materials, thermal power generation, flue gas desulfurization, aerated concrete, magnetic materials, chemical industry, coal water slurry, pellets, slag, ultrafine powder, fly ash, calcium carbonate, quartz sand and other industries.
Castings And Forgings
2. Specification of grinding steel ball:
Inch | Size | T weight(Kg) | Actual Diameter Range (mm) | Material |
Surface hardness (HRC)+/-0.5 |
Core hardness (HRC)+/-0.5 |
Volume |
3/4 ” | D20MM | 0.039+/-0.005 | 19.3~22.3 | B2 | 63-66 | 62-64 | 63-66 |
1 ” | D25MM | 0.075+/-0.01 | 24.5~27.5 | B2 | 63-66 | 62-64 | 63-66 |
1 1/4 ” | D30MM | 0. 14+/-0.02 | 29.7~32.7 | B2 | 63-66 | 62-64 | 63-66 |
1 1/2 ” | D40MM | 0.31+/-0.04 | 39.6~43.6 | B2 | 63-66 | 62-64 | 63-66 |
2” | D50MM | 0.59+/-0.05 | 50~54 | B2 | 62-65 | 61-63.5 | 62-65 |
2 1/2 ” | D60MM | 1.0+/-0.05 | 60.4~64.4 | B2 | 62-65 | 59-61 | 61-64 |
2 1/2 ” | D65MM | 1.25+/-0.07 | 65.6~70.6 | B2 | 62-65 | 59-61 | 61-64 |
2 1/2 ” | D65MM | 1.25+/-0.07 | 65.6~70.6 | B3 | 61-63 | 58-60 | 58-62 |
3” | D75MM | 1.9+/-0. 1 | 76~81 | B2 | 61-63 | 59-62 | 60-63 |
3” | D75MM | 1.9+/-0. 1 | 76~81 | B3 | 61-63 | 58-60 | 58-62 |
3 1/2” | D90MM | 3. 1+/-0. 15 | 88~93.5 | B3 | 60-62 | 57-60 | 59-62 |
3 3/4” | D94MM | 3.5+/-0.2 | 92~97.5 | B3 | 60-62 | 57-60 | 59-62 |
4” | D100MM | 4. 1+/-0.2 | 98~103 | B3 | 60-62 | 57-60 | 59-62 |
4.2” | D105MM | 4.76+/-0.2 | 103~108 | B3 | 59-62 | 57-60 | 59-62 |
4.5” | D115MM | 6.3+/-0.2 | 113~118 | B3 | 59-62 | 57-60 | 58-62 |
5” | D125MM | 8.2+/-0.3 | 123~128.5 | B3 | 58-62 | 57-60 | 58-62 |
Castings And Forgings
Material
C | Si | Mn | P≤ | S≤ | Cr | Ni ≤ | Cu≤ | |
B2 | 0.72-0.86 | 0. 15-0.37 | 0.70-0.80 | 0.035 | 0.035 | 0.20-0.60 | 0.25 | 0.25 |
B3 | 0.58-0.66 | 1.30- 1.90 | 0.40-0.80 | 0.035 | 0.035 | 0.70-0.90 | 0.25 | 0.25 |
Castings And Forgings
Castings And Forgings
Castings And Forgings
After-sales service
LUOYANG ZHONGTAI INDUSTRIES able to provide:
1. ENGINEERED SPARES - DESIGN AND MANUFACTURING
2. LARGE VOLUME STEEL AND IRON CASTING FOUNDARIES
3. HUGE MACHINE SHOP CAPABILITIES
4. TRAINING PROGRAMMES
5. PREVENTATIVE MAINTENANCE PROGRAMS
6. PREVETATIVE MAINTENANCE SERVICES
7. COMPREHENSIVE MAINTENANCE PROGRAMS
Contact Person: Mr. David
Tel: 86-18637916126